From: Investigation into a practical approach and application of cotton fiber elongation
 | Mic | UHML/mm | UI/% | Tenacity/(g·tex−1) | Elongation/% | ES/(g·tex−1) | Work to break/(N·m2·kg−1) |
---|---|---|---|---|---|---|---|
2017 NCVT | Â | Â | Â | Â | Â | Â | Â |
Average | 4.4 | 29.8 | 84.0 | 34.8 | 7.6 | 4.7 | 41.4 |
Minimum | 3.5 | 26.6 | 79.5 | 29.0 | 5.9 | 3.5 | 30.8 |
Maximum | 5.3 | 35.7 | 87.8 | 43.5 | 9.3 | 6.4 | 48.6 |
Intra-sample CV/% | Â | Â | Â | Â | Â | Â | Â |
Average | 3.2 | 2.4 | 1.2 | 4.3 | 5.4 | 7.8 | 5.8 |
Minimum | 0.6 | 0.7 | 0.4 | 1.3 | 1.3 | 1.1 | 1.5 |
Maximum | 13.9 | 6.7 | 1.9 | 7.5 | 17.3 | 17.4 | 18.9 |
2018 NCVT | Â | Â | Â | Â | Â | Â | Â |
Average | 4.7 | 30.5 | 83.4 | 34.3 | 7.7 | 4.8 | 40.8 |
Minimum | 4.2 | 27.7 | 80.9 | 29.5 | 4.9 | 2.9 | 25.8 |
Maximum | 5.3 | 34.0 | 86.3 | 40.4 | 10.5 | 6.8 | 50.6 |
Intra-sample CV/% | Â | Â | Â | Â | Â | Â | Â |
Average | 1.9 | 1.9 | 1.2 | 3.3 | 3.7 | 6.0 | 3.8 |
Minimum | 0.8 | 0.4 | 0.6 | 1.2 | 1.6 | 3.3 | 0.9 |
Maximum | 5.2 | 3.0 | 2.2 | 6.6 | 7.1 | 10.7 | 9.5 |
Elongation calibration cottons | Â | Â | Â | Â | Â | Â | Â |
Low | 5.1 | 29.2 | 80.0 | 33.4 | 5.2 | 6.4 | 26.9 |
Low CV/% | 1.2 | 1.9 | 1.2 | 2.8 | 4.7 | 7.2 | 2.4 |
High | 5.0 | 26.4 | 79.4 | 29.9 | 9.0 | 3.4 | 43.5 |
High CV/% | 0.9 | 3.0 | 1.0 | 3.4 | 3.0 | 5.9 | 2.7 |